Aluminium
Metallic pieces
under friction
Wear resistant
High temperature
resistant
Multi purpose
3475 A&B
Metal Set A1
3479 A&B
Metal Set HTA
3474 A&B
Metal Set M
Metallic pieces under
high compression
Putty
3478 A&B
Superior Metal
Loctite
®
Hysol
®
3475 A&B
Metal Set A1
• Aluminium putty
• Low shrinkage on cure (0.1%)
• Temperature resistant (120°C)
Loctite
®
Hysol
®
3475 A&B is an
aluminium filled, non-sagging,
2K-Epoxy adhesive for repairing
and rebuilding worn metal parts.
Ideal for repairing castings and
cracks in housings and machine
parts.
Loctite
®
Hysol
®
3479 A&B
Metal Set HTA
• Aluminium putty
• Low shrinkage on cure (0.2%)
• High temperature resistant
(190°C)
Loctite
®
Hysol
®
3479 A&B is an
aluminium filled, non-sagging,
2K-Epoxy adhesive for repairing
and rebuilding worn metal parts
in high operating temperature
applications. Ideal for repairing
castings and cracks in housings
and machine parts.
Loctite
®
Hysol
®
3478 A&B
Superior Metal
• Steel putty
• Low shrinkage on cure (0.1%)
• High compression strength
• High temperature strength
(120°C)
Loctite
®
Hysol
®
3478 A&B is a
ferro-silicon filled, non-sagging,
2K-Epoxy adhesive, for repairing
and rebuilding worn metal parts
in areas under high compression
loads. Ideal for shafts, bearing
seats and parallel key
assemblies.
Loctite
®
Hysol
®
3474 A&B
Metal Set M
• Self-lubricating
• High wear resistant
• Temperature resistant (120°C)
Loctite
®
Hysol
®
3474 A&B is a
mineral filled, non-sagging,
2K-Epoxy adhesive which forms
a self-lubricating surface to
reduce sliding wear on moving
parts. Ideal for metallic surfaces
under friction.
2K-Epoxy 2K-Epoxy 2K-Epoxy 2K-Epoxy
1:1 1:1 4:1 1:1
100:100 100:100 7.25:1 100:100
45min. 40min. 20min. 45min.
180min. 150min. 120min. 180min.
Grey Grey Dark grey Grey
Putty Putty Putty Putty
20N/mm
2
20N/mm
2
17N/mm
2
20N/mm
2
70N/mm
2
90N/mm
2
125N/mm
2
70N/mm
2
up to 120°C up to 190°C up to 120°C up to 120°C
500g tub kit 500g tub kit 450g tub kit 500g tub kit